Brick red V0 PA66 with 30% glass fiber reinforced PA66 GF30 plastic resin

Brick Red V0 PA66 with 30% Glass Fiber Reinforced PA66 GF30 Plastic ResinGlass fiber reinforced nylon PA66 is made of PA66 resin and filled with 10-40% glass fiber.It is high strength, high toughness, wear resistance and corrosion resistance. Also, the material is dimensionally stable with high heat deflection temperature, good

Featured Products

Brick Red V0 PA66 with 30% Glass Fiber Reinforced PA66 GF30 Plastic Resin
Brick Red V0 PA66 with 30% Glass Fiber Reinforced PA66 GF30 Plastic Resin
Glass fiber reinforced nylon PA66 is made of PA66 resin and filled with 10-40% glass fiber.

It is high strength, high toughness, wear resistance and corrosion resistance. Also, the material is dimensionally stable with high heat deflection temperature, good electrical insulation, good surface smoothness, easy molding and other advantages.

Material is approved by RoHS compliant, and can be widely used in automotive parts, electronic appliances, power tools, gears, mechanical parts and other fields.
PA66 (F0105 NC)
 Product Description Applications
·PA66· Injection molding
·  Excellent toughness· Good mechanical properties balance
 Properties Test Method Test Condition UnitTypical Values
Physical properties
Specific Gravity ISO 118323ºC g/cm31.085
Mechanical properties
Tensile Strength ISO 527 50mm/min MPa 53.3
Elongation at BreakISO 527 50mm/min %39.9
Tensile Modulus ISO 527 1mm/min MPa 2060
Flexural StrengthISO 17880*10*4MPa 70
Flexural Modulus ISO 1782mm/min MPa 1750
Charpy Notched Impact Strength     ISO 179-1eA23ºCkJ/m2 75
Charpy Notched Impact Strength     ISO 179-1eA-30ºC/4hkJ/m2 14
Thermal properties
Heat deflection temperatureISO 751.80MPaºC68.1
Heat deflection temperatureISO 750.45MPaºC145
Melting PointDSC-ºC255
Other properties
Flammability UL94 1.6mm HB
Note: The data above is typical value for reference, not guarantee value. The data will vary with tool design such as gate type , gate location, gate number, injection molding process and part thickness. The data will vary with different color as well. Prior to use the material, please consult with TOPO NEW MATERIAL CO.,LTD.
 Processing Conditions Range 
Melt Temperature245-260ºC
Mold Temperature60-70ºC
Injection Speed65-80%
Pre-Dry needed120ºC, 2h
Note: The above process condition is only for reference. The actual process should be adjusted according to different type of machine,  mold design and product design.

Brick Red V0 PA66 with 30% Glass Fiber Reinforced PA66 GF30 Plastic Resin
Brick Red V0 PA66 with 30% Glass Fiber Reinforced PA66 GF30 Plastic ResinBrick Red V0 PA66 with 30% Glass Fiber Reinforced PA66 GF30 Plastic ResinBrick Red V0 PA66 with 30% Glass Fiber Reinforced PA66 GF30 Plastic ResinBrick Red V0 PA66 with 30% Glass Fiber Reinforced PA66 GF30 Plastic ResinBrick Red V0 PA66 with 30% Glass Fiber Reinforced PA66 GF30 Plastic ResinBrick Red V0 PA66 with 30% Glass Fiber Reinforced PA66 GF30 Plastic ResinBrick Red V0 PA66 with 30% Glass Fiber Reinforced PA66 GF30 Plastic ResinBrick Red V0 PA66 with 30% Glass Fiber Reinforced PA66 GF30 Plastic ResinBrick Red V0 PA66 with 30% Glass Fiber Reinforced PA66 GF30 Plastic Resin

Are you trading company or manufacturer?

We are manufacturer.

 

About Sample?

5 KG Free Sample can be offered per your request.

 

About Material Color?

We can make the material to your appointed color according to Pantone/RAL#.


How does your factory control the quality?
Quality is the Priority, we always pay great important to quality from beginning to  end, we have  professional QC  for item quality from spare parts to finished goods.

 

 How many days for mass production?

20 days after all artwork and 30% deposit are confirmed.
 

 How can I get the samples? is the sample free? 

7-10 days to send free samples by DHL, TNT, UPS

Contact us

Please feel free to give your inquiry in the form below We will reply you in 24 hours